第一作者：梁小龙 罗洪杰 LIN Hao LU Xiaotong WU Linli

发表刊物：Journal Wuhan University of Technology, Materials Science Edition

摘要：Al foam sandwich panel(AFS) with metallic bonding was fabricated by foaming a hotpressed three-layer composite with two steel facesheets and a melt route precursor as core. The melt route precursor was fabricated by dispersing undecomposed blowing agent into molten Al, followed by solidification. Microstructures of the joints during fabrication process were analyzed by scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS). Static three-point bending was conducted to evaluate joint quality of the AFS. It was found that a primary bonding was achieved by hot-pressing and significant diffusion layer of Fe-Al intermetallic compounds was sustained between steel and Al foam core by foaming. Damage modes of the AFS under three-point bending were dominated by indentation, plastic hinges, core shear and crack. Delamination between steel and foam was absent, implying that reliable metallic bonding was achieved. This method allows for producing large-scale AFS with steel facesheets.

是否译文：否